LSAW Steel Pipe

The UOE LSAW STEEL PIPE mill features the most advanced technology and process, achieves high production efficiency, stable product quality and is equipped with complete inspection equipment. UOE mill adopts U & O forming, the formed pipes are welded inside through five internal welding stations with three wires, and welded outside through four external welding stations with three wires. In accordance with different requirements of the customers, the welded pipe can be expanded either by mechanical or hydrostatic expand to improve dimensional accuracy, and eliminate residual stress.

Specifications

Outside Diameter 508mm- 1118mm (20″- 44″)
Wall Thickness: 6.0-25.4mm 1/4″-1″
Quality Standards: API、DNV、ISO、DEP、EN、ASTM、DIN、BS、JIS、GB、CSA
Length: 9-12.3m (30′- 40′)
Grades: API 5L A-X90,GB/T9711 L190-L625

JOCE SLAW STEEL PIPE is large diameter longitudinal submerged arc welded (SAWL) pipe production line in China. The mill adopts progressive bending process, featuring evenly distributed forming stress, high uniformity of dimension, infinite sizes variation&wide poduct range, and high flexibility, etc.

Specifications

Outside Diameter：Φ406mm- 1626mm (16″ – 64″ )
Wall Thickness：6.0- 75mm (1/4″ – 3″ )
Quality Standards：API、DNV、ISO、DEP、EN、ASTM、DIN、BS、JIS、GB、CSA
Length：3-12.5m ( 10′- 41′ )
Grades：API 5L A-X100, GB/T9711 L190-L690

Tolerance of Outside Diameter and Wall Thickness

Types	Standard
Types	SY/T5040-2000	SY/T5037-2000	SY/T9711.1-1977	ASTM A252	AWWA C200-97	API 5L PSL1
Tube end OD deviation	±0.5%D	±0.5%D	-0.79mm～+2.38mm	<±0.1%T	<±0.1%T	±1.6mm
Wall thickness	±10.0%T	D<508mm, ±12.5%T	-8%T～+19.5%T	<-12.5%T	-8%T～+19.5%T	5.0mm<T<15.0mm, ±0.11
Wall thickness	±10.0%T	D>508mm, ±10.0%T	-8%T～+19.5%T	<-12.5%T	-8%T～+19.5%T	T≥15.0mm, ±1.5mm

Chemical Composition and Mechanical Properties

Standard	Grade	Chemical Composition(max)%					Mechanical Properties(min)
Standard	Grade	C	Mn	Si	S	P	Yield Strength(Mpa)	Tensile Strength(Mpa)
GB/T700-2006	A	0.22	1.4	0.35	0.050	0.045	235	370
	B	0.2	1.4	0.35	0.045	0.045	235	370
	C	0.17	1.4	0.35	0.040	0.040	235	370
	D	0.17	1.4	0.35	0.035	0.035	235	370
GB/T1591-2009	A	0.2	1.7	0.5	0.035	0.035	345	470
	B	0.2	1.7	0.5	0.030	0.030	345	470
	C	0.2	1.7	0.5	0.030	0.030	345	470
BS En10025	S235JR	0.17	1.4	-	0.035	0.035	235	360
	S275JR	0.21	1.5	-	0.035	0.035	275	410
	S355JR	0.24	1.6	-	0.035	0.035	355	470
DIN 17100	ST37-2	0.2	-	-	0.050	0.050	225	340
	ST44-2	0.21	-	-	0.050	0.050	265	410
	ST52-3	0.2	1.6	0.55	0.040	0.040	345	490
JIS G3101	SS400	-	-	-	0.050	0.050	235	400
JIS G3101	SS490	-	-	-	0.050	0.050	275	490
API 5L PSL1	A	0.22	0.9	-	0.03	0.03	210	335
	B	0.26	1.2	-	0.03	0.03	245	415
	X42	0.26	1.3	-	0.03	0.03	290	415
	X46	0.26	1.4	-	0.03	0.03	320	435
	X52	0.26	1.4	-	0.03	0.03	360	460
	X56	0.26	1.1	-	0.03	0.03	390	490
	X60	0.26	1.4	-	0.03	0.03	415	520
	X65	0.26	1.45	-	0.03	0.03	450	535
	X70	0.26	1.65	-	0.03	0.03	585	570